Study of Biaxial Mechanical Properties of the Passive Pig Heart: Material Characterisation and Categorisation of Regional Differences

Regional mechanics of the heart is vital in the development of accurate computational models for the pursuit of relevant therapies. Challenges related to heart dysfunctioning are the most important sources of mortality in the world. For example, myocardial infarction (MI) is the foremost killer in sub-Saharan African countries. Mechanical characterisation plays an important role in achieving accurate material behaviour. Material behaviour and constitutive modelling are essential for accurate development of computational models. In most cases previously, the mechanical properties of the heart myocardium were assumed to be homogeneous. The main objective of this paper is to determine the mechanical material properties of healthy porcine myocardium in three regions, namely left ventricle (LV), mid-wall/interventricular septum (MDW) and right ventricle (RV). The biomechanical properties of the pig heart RV, LV and MDW were characterised using biaxial testing. The biaxial tests show the pig heart myocardium behaves non-linearly, heterogeneously and anisotropically. In this study, it was shown that RV, LV and MDW may exhibit slightly different mechanical properties. Data presented here may be helpful in regional tissue mechanics, especially for the understanding of various heart diseases and development of new therapies.


Introduction
Globally, cardiovascular diseases are posing challenges to public health 1 . In sub-Saharan Africa, these diseases remain problematic since the majority of the population are adversely affected 2 . Challenges related to heart dysfunctioning are the most important sources of mortality in the world. For example, myocardial infarction (MI) is the foremost killer in sub-Saharan African countries 3 . Mechanical characterisation is important in achieving accurate material behaviour. The understanding of biomechanical properties of soft tissue plays a vital role in the development and application of computational models for various diseases [4][5][6][7] . It may also lead to accurate comprehension of different disease mechanisms such as MI. The precise understanding of the mechanical behaviour of the heart myocardium in different regions of the heart may assist in the development of accurate constitutive models. This may lead to the development of new therapies and also to the improvement of current therapies. The passive and active properties of heart walls play a pivotal role in understanding its pathophysiological and physiological functions. This could be utilised in the development of accurate and successful surgical procedures as well as in the full development of medical devices and their optimum design, including the design of prostheses 8,9 . For most cardiovascular diseases, especially congenital heart disease, the evolution in the development of accurate and patient-specific computational models could assist in accurate predictive conditions 5,[10][11][12][13] .
In most cases previously, the mechanical properties of the heart myocardium have been assumed to be homogeneous in the development of computational models to determine the global functioning of the heart 4,6,14,15 . It has been clearly demonstrated that the mechanical properties of adult ventricles are different from neonatal porcine ventricles 16 . Following the same logic, the mechanical behaviour of various regions in the pig heart may exhibit different stiffness. Furthermore, in most publications, it has been assumed that material properties of rested hearts in various regions, including LV, MDW and RV have the same mechanical properties. Most authors have considered or studied the mechanical behaviour of the LV 6 and RV or both 6,16 . These material properties are then used to develop computational models in understanding various disease mechanisms, including MI. The development of therapies could be achieved by using computational models that have the ability to precisely estimate the regional stresses and strains of tissues 17 . The assumption that heart tissue has the same material properties might not be accurate and if this is the case, the accuracy of computational models could be affected.
Overall, the data for an accurate constitutive model of the MDW remains scarce. The objective of this study was to validate the constitutive model suitable for three heart regions, namely the RV, LV and MDW of the pig heart. This was done systematically by quantifying the material properties of these regions. To achieve this, biaxial tests were performed on the four samples from all three regions of the pig heart. Circumferential and longitudinal loads were performed on the sample. The biaxial testing allowed a study of the effect of applying one load in circumferential direction to the longitudinal direction. To evaluate relevant material parameters for a suitable constitutive model, the average stress-strain curve of the RV, LV and MDW was determined. The comparison of material parameters obtained from two suitable constitutive models is made between the MDW, LV and RV. In addition, these material parameters may be utilised for the development of accurate computational models for studying mechanisms of various cardiovascular diseases.

Material preparations
To achieve the objectives of this study, a local abattoir was contacted to supply four fresh mature porcine hearts from pigs weighing about 104 kg. The collected porcine hearts were collected immediately after slaughter and were stored in ice-cooled boxes at 4 o C during transportation to the biomechanics lab. All the samples were dipped into 0.6% glutaraldehyde for 20 minutes before testing. To ensure accurate experimentation, the porcine hearts were visually inspected for any structural damage before testing. The FSN coordinate system was virtually inspected by looking at the mean-fibre direction (F), the sheet axis direction (S) and the sheet normal direction (N) 18,19 . The samples were dissected into various regions including LV, RV and septal wall. To conduct the biaxial testing, the ventricles were cut into 18 × 18 mm 2 pieces using a squared-shaped cutting punch. All procedures followed the NIH guidelines for the Guide for the Care and Use of Laboratory Animals.

Methods
Due to the irregular thickness of the myocardium of the pig heart, the thickness was measured by ensuring that at least four measurements were taken at various points of the selected sample. For an accurate reading, the four readings taken were then averaged to obtain the average thickness of the myocardium. The load cell of 23 N was used in a CellScale biaxial testing machine. A saline solution was used to keep the sample fresh. Also, the saline solution in the bath was allowed to warm up to 37 o C before any test was conducted. To utilise image tracking, the samples were soaked for 15 minutes in the warm saline bath and then taken out during testing. This was done so as not to compromise the quality of image tracking. The samples were tested using the procedure as described by Ahmad et al. 16 . The image acquisition frequency used in this experiment was 5 Hz.

Biaxial tensile testing equipment
To capture the biomechanical properties of the passive heart tissue, CellScale biaxial equipment was used 20-22 (see Figure 1). The frequency of 10 Hz was used in capturing the force displacement data during biaxial stretching of the myocardium. One sample in each region was cut and the thickness of each sample was measured using a Vernier calliper. All the measurements taken on the sample were recorded to further determine the overall thickness of each sample. 40% strain was then applied to the myocardium while measuring the force and displacements. The allocated load cell of 23 N measured the force in each direction independently 23 . To ensure the accuracy of the fibre direction in the heart myocardium, careful inspections were done to ensure that samples were cut accordingly. Additionally, all the RV, LV and MDW regions were cut into equal pieces of 20 × 20 mm 2 .

Data analysis
The mechanical properties of the passive myocardium of porcine hearts in the LV were quantified and compared to those in the RV and MDW regions. Using the Fung and Choi-Vito models, the anisotropic of the materials was calculated using Equation (13). Stress and strain were determined by using Equation (10) and Equation (2), respectively. Equation (3) was then used to determine the cross-sectional area of the tested myocardium in different passive heart regions. In order to satisfy all conditions, Equation (13) and Equation (14) were used 24,25 . In this study, the constitutive model fitting was done using the Hyperfit software designed for experimental data fitting of hyperelastic materials 26 . The data analysis on this paper is similar to what was presented previously 27 .

Stress and strain
To calculate the stress on the tested tissue, the constant cross-sectional area was assumed to be true. The measured force F was used to calculate the stress applied in the cross-sectional area A of the tissue. Therefore, the stress was calculated as follows:

=
(1) The strain ε was calculated by the following relationships:

Strain field
Strain is regarded as the general measure of deformation in a material subjected to applied force. The scalar product of the two elemental vectors and after deformation was and . The change in scalar product of the two elemental vectors involves a change in length and angle between the two vectors. The material vectors of spatial scalar product .
can be found as follows: Where represents the right Cauchy-Green deformation tensor. This tensor is given in terms of the deformation gradient F as: Alternatively, the left Cauchy-Green or Finger tensor is expressed as follows: The change in scalar product can now be found in terms of the material vectors and and the Lagrangian or Green strain tensor E as: Where is defined as the material tensor

Constitutive modelling
In this study, two constitutive models were considered and utilised in fitting the biaxial experimental data. The first constitutive model is the well-known Fung model 28 . The second constitutive model considered in this study is Choi-Vito, which is similar to the Fung model. The advantage of the Choi-Vito model is that it has three separate exponentials responsible for different fibre directions. The Fung constitutive model is given by the following strain energy function: Q is a quadratic function of three principal strain components. In this case, Q represents the special three-dimensional isotropy with regard to the fibre coordinate system. To account for in-plain shear strains 29 , the full expression of the Fung constitutive model was utilised as shown in Equation (10): Where C, b1, b2, b3, b4, b5 and b6, are absolute constants which are independent of deformation and position in the body. In essence the main function c is to scale stresses. E11 and E22 are the fibre strain and cross-fibre strain, respectively.
> 0, > | |, > | | (13) The first Piola-Kirchhoff tensor P is an asymmetrical two-point tensor and as such is not completely related to the material configuration. It is possible to contrive a totally material symmetric stress tensor, known as the second Piola-Kirchhoff stress S, The Choi-Vito model 30 could be used for modelling soft tissues. In this study, material parameters of the Fung model were compared with those of the Choi-Vito model 31 . The latter has been used for experimental data of various soft tissues including the human coronary artery 17 .
As per the Choi-Vito (1990) model 31 : co, c1, c2 and c4 are all material constants of the Choi-Vito model. The Fung model and Choi-Vito model use the material parameters to determine the stiffness and anisotropy of the material.
To ensure the Choi-Vito model accuracy of material parameters, the following conditions must be satisfied and were utilised as follows: Non-linear stiffness in different directions of the material is determined by the product of × and × . The metric of anisotropy of stiffness is determined by the ratio of and interaction between the different axis is indicated by the product of × .

Results
The two constitutive models were successfully fit to the experimental data. The Choi-Vito model was found to provide the best fit with the experimental data compared to the Fung model. The thickness of RV, LV and MDW varied considerably. Equation (13) was used to determine the anisotropy of the tissue material of the pig heart in the different regions. The RV, LV and MDW showed an anisotropy of (average ± standard deviation) of 0.695 ± 0.110, 0.723 ± 0.212 and 0.650 ± 0.089, respectively. A summary of the Fung constitutive analysis in the RV, LV and MDW in the pig heart is given in Tables 1, 2  (e) (f)    Figure 3 shows the Experimental data of stress-strain curves was calculated using Equation (3) and strain was calculated using Equation (4). The constitutive material parameters for the Fung and Choi-Vito models are presented in Tables 1-8  Equally, the anisotropy of the RV and MDW were found to be close in the Fung model (p = 0.2259). No noteworthy difference in the anisotropy was found between the LV and MDW (p = 0.238). For the Choi-Vito model, the differences in anisotropy between the RV and LV were found to be insignificant (p = 0.165). Additionally, no noteworthy differences in anisotropy were found between the RV and MDW (p = 0.357). The anisotropy of between the RV and MDW using the Choi-Vito model were found to be less significant (p = 0.147). Figure 7 shows the box-plot of the Fung model in comparing the material parameters of the RV, LV and MDW regions of the pig heart. The difference in material parameters of the Choi-Vito model in pig heart regions is shown in Figure 8. Table 1. Material parameters (c, b1, b2, b3, b4, b5, b6) of fitted Fung model Equation (9) Table 8. Choi-Vito model average material parameters (co, c1, c2, c3) in different regions of the porcine heart. The average curve was determined using the same method as described in [36].

Discussion and conclusions
This study shows that the mechanical behaviour of porcine myocardial tissue is non-linear and anisotropic. Most often only the LV is considered [32][33][34] . However, in this study, the overall characteristic of the LV, MDW and RV is consistent with other soft tissues 25,35,36 . Biaxial testing in the LV, MW and RV was conducted. Even though experimental data is available on the LV myocardium of porcine, no biaxial experimental data is available for the RV and MDW. Five fresh porcine hearts were tested using biaxial test equipment. Biaxial deformation was performed on the LV myocardium, RV myocardium and MDW. The biaxial experimental data was fit to the Fung exponential function.
Interesting observations were made regarding the different mechanics of these regions of the pig heart.
To the author's knowledge, this study presents an interesting finding. In most cases previous, the material properties of porcine have been assumed to be the same in all regions of the heart. This means that the computational models developed also depend on this assumption. In this experiment, the material properties of the LV, RV and MDW of the porcine heart were found not to be the same and should be treated as such. The important observation is that the stiffness confident b3 is zero in all regions. As a result of the myocardial tissue structure, the cardiac tissue has been found to show non-linear material behaviour 16,37 . The material behaviour of myocardial tissue in different heart regions may differ based on the variation of the intricate structure.
Mechanical properties of the myocardial tissues play an important role in the development of computational models to study various mechanisms of heart diseases. Inaccuracy in the mechanical properties of the heart region may affect the accuracy of the computational models developed. Computational modelling is increasingly utilised to further understand pathological conditions. Various new interventions and therapies have been developed based on knowledge gained from these computational models.
Regional differences in material parameters in a passive pig heart were found. This finding is similar to that regarding the small intestine, where it was observed that passive small intestine tissue exhibits material parameter differences based on location 38,39 . Similarly, it was also observed that porcine small bowel mesentery may exhibit different material parameters of the Fung model in different regions 40 .
To model the mechanical response of the passive pig heart tissue in three different regions, the Fung model 28 and Choi-Vito model 30 were selected as shown in Figure 2 (a). In Figure 2 (b) the direction of the fibres used during mechanical testing in the passive myocardium is shown. The two constitutive models were also selected based on the accuracy of fit (R 2 ) as shown in Figures 4, 5 and 6. As shown in Tables 3, 4 and 5, the Fung model was able to fit the experimental data as expected. However, the Choi-Vito model (see values of R 2 in Tables 5, 6 and 7) proved to fit the experimental data well. It was found that there is no major difference of R 2 between the fit experimental data using the Fung and Choi-Vito models (see Tables 4 and 8). An average Fung and Choi-Vito model in three different pig heart regions could be utilised for the development of computational models as listed in Tables 4 and 8. Like various soft tissues 19,24,41 , passive myocardium in the three different regions were found to be anisotropic. In this study, the average material parameters in the RV, LV and MDW regions of passive pig heart can be employed in finite element analysis (FEA). FEA may then be utilised to study the mechanisms of MI in different stages by obtaining the average regional stresses and strains of the myocardium.